Benefits of CH liner
|
Insulation, barrier for fluids, reparative dentin, fluoride release, antibac.
|
|
Calcium hydroxide paste system:
1) Base 2) Paste 3) Filler 4) Setting reaction accelerated by: 5) Soluble in water? 6) Setting time? |
1) Base - calcium hydroxide
2) Catalyst = salicylate (weak acid, reacts with calcium) 3) Filler = titanium oxide 4) Water 5) 3 mins 5) Yes |
|
What was the original glass ionomer?
|
ASPA - aluminofluorosilicate glass polyacrylic acid
|
|
What is glass ionomer liquid?
|
Aqueous solution of polyacids
|
|
What are glass ionomer particles?
|
Calciumfluoroaluminum silicate, Barium or ZnO for radioopacity
|
|
Advantages of glass ionomer
|
Chemical bond to tooth , good seal
Leach fluoride Strong Coeffecieint of thermal expansion similar to tooth |
|
Disadvantages of glass ionomer
|
Slow initial set, slow final set
|
|
Glass ionomer adhesion
|
Ioninc bonding with calcium and phosphate ions of tooth tstructure
|
|
Vitrebond
|
light cured glass ionomer, initial set due to photo-initiated polymerization
delayed setting due to acid/base |
|
Glass ionomer vs. RMGI structure?
|
Glass - polyacid chains do not connect
RMGI - polyacid chains connect |
|
What crosslinks polyacid chains in RMGI?
|
Pendent methylacrylate group
|
|
Photopolymerization:
1) Activator 2) Photosensitive intiatiator 3) Accelerator Absorb what wavelength of light? |
1) Visible light
2) Diketone 3) Amine 470 nm (camphoquinone) |
|
Purpose of:
1) CH liner 2) ZOE base |
1) Stimulate reparative dentin
2) added insulation, resistance to condensation during placement of amalgam, temp filling material, base, liner, cement |
|
Main advantage of ZOE
|
neutral ph, eugenol is soothing to pulp if dentin is thick enough (0.5-1.0mm)
|
|
Disadvantages of ZOE:
|
No chemical bonding, highly soluble, irritation to soft tissue if dentin too thin, low strength
|