34 Cards in this Set

  • Front
  • Back
WHAT IS THE MOST IMPORTANT SINGLE FACTOR IN SECURING GOOD PAINT PERFORMANCE
PROPER SURFACE PREPARATION
BEFORE USING ANY NONSKID COMPOUND, YOU SHOULD CONSULT WHICH CHAPTER OF THE NAAL SHIPS TECHNICAL MANUAL
634
WHAT IS THE NONEXTENDABLE SHELF LIFE ASSIGNED TO NONSKID MATERIALS
1 YEAR
WHAT DEGREE SHOULD NONSKID COATINGS BE STORED UNTIL USED
50 TO 90 DEG FAHR
WHAT CAUSES THE MAJORITY OF NONSKID COATING FAILURES
IMPROPER APPLICATION OR APPLICATION OVER A POORLY PREPARED DECK
HOW WILL APPLICATION OF NONSKID MATERIAL ON SURFACES ABOVE 100f AFFECT THE CURE TIME
CURE TIME WILL BE SIGNIFICANTLY DECREASED
WHAT IS THE IDEAL SITUATION IN WHICH TO APPLY THE NONSKID SYSTEM
SHOULD BE APPLIED OVER A WHITE ABRASIVE BLASTED SURFACE THAT IS FREE FROM OIL, GREASE OR OTHER CONTAMINATES. SHOULD BE APPLIED ON A DAY WHEN THE HUMIDITY DOESN'T EXCEED 60% AND THE AIR TEMP RANGES BETWEEN 65 AND 85 DEG FAHR AND THE DECK TEMP IS BELOW 100DEG FAHR
WHAT IS TYPE I NONSKID
GENERAL PURPOSE
WHAT IS COMPOSITION G
GENERAL USE ABRASIVE
WHAT IS COMP L
LIMITED USE AIRCRAFT CARRIER LANDING AND RUN OUT AREA
WHAT TYPE OF NONSKID USED FOR WEATHER DECKS, ALL EXTERIOR PASSAGEWAYS AND SOME INTERIOR DECKS AND PASSAGEWAYS ON ALL SHIPS
TYPE I OR II, COMPOSITION G OR L, GRADE B, CLASS 1 OR 2
WHAT TYPE OF NONSKID USED ON HELIPADS AND HANGER DECKS
ROLLABLE TYPE, TYPE I, COMP G, GRADE A, CLASS 1
WHERE WOULD U USE TYPE III, COM L, GRADE B, CLASS 1 OR 2
ON WOODEN DECKS OR WHERE FLEXIBILITY IS REQUIRED
WHAT NONSKID SYSTEM IS INTENDED FOR USE IN CARRIER LANDING AREAS
TYPE I, COMP L, GRADE B, CLASS 1
WHAT IS THE MOST EFFECTIVE METHOD OF REMOVING WORN NONSKID
CENTRIFUGAL BLASTING
WHAT IS ABRASIVE BLASTING
PROCESS IN WHICH THE NONSKID COATING IS REMOVED AND A 2-4 MIL PROFILE IS LEFT IN THE DECK METAL
WHAT ABRASIVES ARE USED TO CLEAN STEEL SURFACES ON DECK
CHILLED IRON, STEEL ABRASIVE, AND ALUMINUM OXIDE
what should u do when an aluminum deck is not painted immediately after being cleaned or when it has been contaminated with oil or grease
washed with a liquid detergent cleaner, type II, cleaning compound, thoroughly rindsed with freshwater, and allowed to dry completely
CONTROLLING THE STANDARD MIL PROFILE IS DEPENDENT ON WHAT FACTORS
THE SIZE OF THE SHOT IN RELATION TO THE SPEED OF THE BLASTING MACHINE
WHAT PERCENT OF EACH SQUARE INCH OF SURFACE MUST BE FREE OF ALL VISIBLE RESIDUES AFTER A BLASTING OPERATION
AT LEAST 95 PERCENT
HOW SOON AFTER THE METAL DECKS ARE CLEANED SHOULD THE PRIMER BE APPLIED
WITHIN 1 HOUR AFTER THE METAL IS CLEANED. LESSENS THE POSSIBILITY OF RUSTIN
WHY IS THE USE OF AIR POWERED TOOLS PREFERRED TO ABRASIVE BLASTING WHEN PREPARING DECKS FOR NONSKID COATINGS
BECAUSE THERE IS LESS RISK OF CONTAMINATION, BASICALLY LESS DAMAGE
WHAT IS THE PURPOSE OF THE TENNANT MACHINE
IS A ROTARY DESCALER AND DECK PEENING MACHINE. USED TO REMOVE OLD PAINT AND NONSKID FROM STEEL OR ALUMINUM
WHAT IS THE GENERAL RULE FOR SELECTING THE APPROPRIATE TOOL TO USE FOR SURFACE PREPARATION OF NONSKID
SELECT THE FASTEST METHOD OF REMOVAL THAT WILL CAUSE THE LEAST DAMAGE TO THE UNDERLYING METAL SURFACE
WHAT IS THE BEST METHOD OF APPLYING NONSKID TO HEAVY WEAR AREAS, SUCH AS FLIGHT DECKS
ROLLING OR TROWELING
HOW IS THE SURFACE CLEANED WHEN USING SOLVENTS
WIPED WITH CLEAN LINT FREE RAGS SOAKED IN SOLVENT AND WIPED DRY WITH CLEAN LINT FREE RAGS WHILE IT IS STILL WET
WHAT IS AN INDICATION THAT A NONSKID SURFACE SHOULD BE OVERCOATED
WORN SMOOTH, BUT RETAINS GOOD ADHESION WITH NO BARE AREAS
HOW THICK IS THE ANTICORROSIVE PRIMER APPLIED OVER A STEEL SURFACE PROFILE
2 TO 4 MILS DRY FILM THICKNESS OVER THE MEASURED SURFACE PROFILE
HOW MAY NONSKID EPOXY PRIMERS BE APPLIED
BRUSHING, ROLLER COATING OR SPRAYING
WHEN USING THE ROLLER METHOD OF APPLYING EPOXY HOW MANY COATS ARE REQUIRED
TWO COATS
WHAT IS THE POT LIFE OF AN EPOXY MIXTURE AFTER COMPONENTS ARE MIXED TOGETHER
6 HOURS AT 70 DEG FAHR
WHAT IS THE TIME FRAME NONSKID SHOULD BE APPLIED FOR OPTIMUM ADHESION
WITHIN 24 HOURS AFTER THE PRIMER HAS CURED
WHAT SOLVENT IS USED TO CLEAN MATERIALS USED IN THE APPLICATION OF NONSKID COATINGS
XYLENE
WHAT MANUAL REFER TO FOR SPECIFIC GUIDELINES
NAVAL SHIPS TECHNICAL MANUAL CHAPTER 634