WHAT ARE CRACKS AND SMALL SURFACE FISSURES IN TRANSPARENT PLASTIC MATERIALS CALLED?
|
CRAZING.
|
|
WHAT SHOULD YOU USE TO CLEAN EXCESSIVE MASKING PAPER ADHESIVE RESIDUE FROM PLASTIC?
|
ALIPHATIC NAPHTHA.
|
|
WHAT IS NORMALLY USED TO MEASURE SCRATCHES ON PLASTIC MATERIALS?
|
OPTICAL MICROMETER.
|
|
TO SAND OUT SCRATCHES IN TRANSPARENT PLASTIC, WHAT IS THE MAXIMUM COARSE NUMBER OF ABRASIVE PAPER THAT YOU MAY USE?
|
No.240A.
|
|
WHAT SUBSTANCE IS OFTEN APPLIED TO THE BUFFING WHEEL IN PLACE OF,OR IN ADDITION TO, A BUFFING COMPOUND THAT ACTS SIMILAR TO WAX TO FILL HAIRLINE SCRATCHES AND PROVIDES A HIGH GLOSS TO PLASTIC SURFACES?
|
PLAIN TALLOW.
|
|
HOW MANY TIMES GREATER WILL PLASTICS EXPAND AND CONTRACT AS COMPARED TO METAL?
|
THREE(3) TIMES GREATER.
|
|
WHEN REPAIRING THE SURFACE OF REINFORCED PLASTIC AND SANDWICH CONSTRUCTION LAMINATES, WHAT SHOULD YOU USE OVER THE BUILD-UP REPAIR AREA TO WORK OUT EXCESS RESIN AND AIR BUBBLES?
|
CELLOPHANE.
|
|
IN ADDITION TO THE STEPPED METHOD, WHAT OTHER METHOD OF REPAIR MAY BE USED TO PLY DAMAGE TO SOLID LAMINATES?
|
SCARFED METHOD.
|
|
WHAT TYPE OF COATING IS FREQUENTLY USED TO PROTECT FRONTAL SURFACES OF REINFORCED PLASTICS EXPOSED TO HIGH SPEEDS?
|
RAIN EROSION COATING.
|
|
A HOLE, BREAK, OR CRACK IN ONE OR BOTH FACINGS, RESULTING IN DAMAGE TO THE HONEYCOMB/CORE IS REFERRED TO AS WHAT TYPE OF DAMAGE?
|
PUNCTURE DAMAGE.
|
|
WHAT TYPE OF REPAIR PATCH IS NORMALLY USED TO ENSURE AERODYNAMIC SMOOTHNESS ON A/C CONTROL SURFACES?
|
FLUSH PATCH.
|
|
ADVANCED COMPOSITE MATERIALS CONSIST OF A COMBINATION OF WHAT MATERIALS?
|
A COMBINATION OF HIGH-STRENGTH STIFF FIBERS EMBEDDED IN A COOMON MATRIX (BINDER) MATERIAL.
|
|
WHAT TYPE OF INSPECTION IS USED TO ANALYZE THE EXTENT OF THE DAMAGE AND EFFECTIVENESS OF REPAIR TO COMPOSITE MATERIALS?
|
NONDESTRUCTIVE INSPECTION.
|
|
WHAT TYPES OF FIBERS ARE GOLDEN YELLOW IN COLOR AND ARE USED IN MANY SECODARY STRUCTURES REPLACING FIBER GLASS OR AS A HYBRID WITH FIBER GLASS?
|
KEVLAR FIBERS.
|
|
WHAT IS USED AS A SINGLE PLY-ARRANGMENT OF UNIDIRECTIONAL OR WOVEN FIBERS IN A MATRIX?
|
LAMINA.
|
|
CRAZING AND CRACKING OF A COMPOSITE MATERIALS BY ULTRAVIOLET RADIATIONIS CATEGORIZED OF WHAT TYPE OF DAMAGE?
|
ENVIRONMENT DAMAGE.
|
|
WHAT TYPE OF DAMAGE INSPECTION
METHOD IS LIMITED TO FINDING DEFECTS CLOSE TO THE SURFACE IN COMPOSITE MATERIALS? |
TAP TEST.
|
|
WHAT DOES A DARK AREA ON DEVELOPPED FILM INDICATE WHEN VIEWING AN X-RAY OF COMPSITE MATERIALS?
|
A THINNER AREA OF A PART.
|
|
"AS IS" DAMAGE IS CLASSIFIED AS WHAT TYPE OF DAMAGE?
|
NEGLIGIBLE DAMAGE.
|
|
DAMAGE TO THE A/C'S SKIN THAT CANNOT BE ALLOWED TO REMAIN "AS IS" IS CLASSIFIED AS WHAT TYPE OF DAMAGE?
|
REPAIRABLE DAMAGE.
|
|
WHERE CAN YOU FIND INFORMATION ABOUT STRUCTURAL DAMAGE CLASSIFICATION, INSPECTION PROCEDURES, TYPICAL REPAIR PROCEDURES, AND TOOL AND MATERIALS LISTS?
|
THE AIRCRAFT'S STRUCTURAL REPAIR MANUAL (SRM).
|
|
WHAT IS THE CLASSIFICATION OF DAMAGE WHEN WATER GETS TRAPPED
IN A HONEYCOMB AREA? |
CLASS VII.
|
|
WHAT ENABLES YOU TO IDENTIFY AND CLASSIFY A/C DAMAGE BY CONFINING THE REPAIRS TO LOAD-CARRYING REQUIREMENTS?
|
REPAIR ZONES.
|
|
WHAT ARE THE MOST CRITICAL ZONES IN DEFINING AERODYNAMIC SMOOTHNESS OF CONTROL SURFACES?
|
LEADING EDGES OF WINGS AND TAILS, FWD NACELLES AND INLET AREAS, AND FWD FUSELAGES.
|
|
WHAT IS A GOOD TOOL FOR REMOVING SMALL AREAS OF DAMAGE ON LAMINATES, ALTHOUGH IT HAS A TENDENCY TO DAMAGE THE HONEYCOMB CORE?
|
A HOLE SAW.
|
|
WHAT TYPE OF DUST AND PARTICLES ARE CONDUCTORS, CAN CAUSE SHORTS IN ELECTRICAL EQUIPMENT, AND CONTAMINATE HYDRAULIC SYSTEMS?
|
GRAPHITE.
|
|
WHEN MAKING BONDED REPAIRS, WHAT MATERIALS PRESENT HEALTH AND FIRE HAZARDS TO PERSONNEL?
|
SOLVENTS.
|
|
WHAT TYPES OF COMPOSITE MATERIAL PARTICLES AND DUST CANNOT BE DISPOSED OF BY BURNING AND MUST BE PACKAGED, TAGGED AND BURIED IN AN APPROVED LANDFILL?
|
CARBON AND GRAPHITE FIBERS.
|
|
WHAT IS THE PRIMARY OBJECTIVE OF ANY PAINT FINISH?
|
TO PROTECT EXPOSED SURFACES AGAINST CORROSION AND DETERIORATION.
|
|
HOW CAN YOU IDENTIFY THE PAINT SYSTEM OF AN AIRCRAFT?
|
A DECAL OR STENCIL LOCATRD ON THE RIGHT SIDE OF THE A/C AFT FUSELAGE.
|
|
BY WHAT MEANS SHOULD CHEMICAL OR MECHANICAL PAINT REMOVAL BE ACCOMPLISHED?
|
THE MILDEST MEANS POSSIBLE.
|
|
WHAT APPEARANCE SHOULD CHEMICAL PAINT STRIPPER HAVE THAT INDICATES THE PAINT IS READY TO BE REMOVED?
|
WRINKLED APPEARANCE.
|
|
WHAT TREATMENT IS AN EXTREMELY IMPORTANT PART OF THE CORROSION CONTROL PROCESS?
|
CHEMICAL CONVERSION.
|
|
WHAT IS THE POT LIFE OF EPOXY-POLYAMIDE PRIMER ONCE THE TWO PARTS ARE MIXED?
|
EIGHT (8) HOURS.
|
|
WHAT TYPE OF EVALUATION SHOULD ALL PERSONNEL RECEIVED
PRIOR TO BEING ASSIGNED DUTIES INVOLVING THE MIXING AND APPLICATION OF POLYURETHANE PAINT SYSTEM COATINGS? |
A PREPLACEMENT AND PERIODIC MEDICAL EVALUATION.
|
|
WHAT IS THE CLOSEST DISTANCE THAT UNPROTECTED PERSONNEL SHOULD BE ALLOWED TO NEWLY PAINTED SURFACES UPON COMPLETION OF THE PAINTING OPERATION?
|
FIFTEEN (15) FEET.
|
|
FOR EXCELLENT ADHESION, WHAT IS THE DRYING PERIOD FOR ELASTROMERIC RAIN EROSION-RESISTANT COATING?
|
SEVEN (7) DAYS.
|
|
REGARDING PAINTING SPECIFICATIONS FOR LETTERS AND NUMERALS, HOW IS THE SPACE MEASUREMENT BETWEEN LETTERS AN NUMERALS DETERMINED?
|
IT ALWAYS ONE-SIXTH(1/6) OF THE HEIGHT OF THE LETTER OR NUMERAL.
|
|
WHAT ARE TACTICAL PAINT SCHEME PATTERNS BASE ON?
|
OPTICAL PRINCIPLES.
|
|
WHAT TYPE OF PAINT SPRAY GUN IS DESIGNED FOR SMALL JOBS?
|
SUCTION-FEED TYPE.
|
|
WHAT IS THE PROBABLE CAUSE IF YOUR PAINT SPRAY GUN IS LEAKING IN THE FRONT?
|
THE FLUID NEEDLE IS NOT SEATING PROPERLY.
|
|
WHAT IS THE DESIRABLE DISTANCE FROM THE SURFACE THAT YOU SHOULD HOLD THE SPRAY GUN IN ORDER TO GET THE PROPER COVERAGE AND A SMOOTH COAT OF PAINT.
|
BETWEEN SIX(6) TO TEN (10) INCHES.
|
|
WHAT MAY CAUSE DUSTING AND RIPPLING IN A PAINT FINISH?
|
EXCESSIVE AIR PRESSURE.
|
|
BASIC SEALANTS ARE CLASSIFIED IN HOW MANY GENERAL CATEGORIES?
|
THREE(3) PLIABLE, DRYING, AND CURING.
|
|
WHAT IS USED TO APPLY CLASS B SEALING MATERIALS?
|
AN EXTRUSION GUN AND SPATULA.
|